La2O3
Hirosaki, N.Ogata, S.Kocer, C.
Journal of Alloys Compd. (2003) 351, 31-34
a=3.936Å b=3.936Å c=6.166Å
α=90° β=90° γ=120°
Ce2O3
a=3.941Å b=3.941Å c=6.182Å
Nd2O3
a=3.859Å b=3.859Å c=6.072Å
Hirosaki, N.Kocer, C.Ogata, S.
a=11.392Å b=11.392Å c=11.392Å
α=90° β=90° γ=90°
a=11.41Å b=11.41Å c=11.41Å
a=11.176Å b=11.176Å c=11.176Å
Gd2O3
a=10.812Å b=10.812Å c=10.812Å
Dy2O3
a=10.67Å b=10.67Å c=10.67Å
Lu2O3
a=10.358Å b=10.358Å c=10.358Å
O3Pr2
a=3.895Å b=3.895Å c=6.126Å
O3Pm2
a=3.819Å b=3.819Å c=6.023Å
a=11.065Å b=11.065Å c=11.065Å
O3Sm2
a=10.995Å b=10.995Å c=10.995Å
a=11.288Å b=11.288Å c=11.288Å